Performance of surface ionic conduction single chamber fuel cell prepared by the sol gel method

The performance of surface ionic conduction single chamber fuel cell (SIC‐SCFC) prepared by the sol gel method was studied on electric characteristics due to the differences of the operating temperature and humidity, the electrode distance and electrolyte film depth, and multiple cells with the series and parallel connections. The SIC–SCFC was arranged the both anode of Pt and cathode of Au on the boehmite electrolyte. The open circuit voltage (OCV) of single cell achieved a maximum of 530mV in the dry gas mixtures of O₂/H₂=50% in room temperature operation, and but it became decrease as over 60%. The OCV was maintained the constant value between operating temperatures of 30°C to 80°C, and but it was decreased sharply at over 90°C because a humidity on the cell became lower as increasing operating temperature. Then, the cell property was improved to 120°C by adding to the humidity of 70% using a humidifier. The electrode distance and the electrolyte film depth of SIC‐SCFC found to be contributed to the reductions of the cell resistance and the surface roughness on the electrode, respectively. Moreover, the power property of SIC‐SCFC was significantly improved by cell stacks comprised of the series or parallel connection of a cell.     

Direct and controlled device integration of graphene oxide on Quartz Crystal Microbalance via electrospray deposition for stable humidity sensing

Integration of advanced and functional materials onto conventional sensing platforms can improve the device performances and even discover new applications. For piezoelectric resonant sensors, an addition of sensing materials can induce damping and hinder a stable device operation. Hence, the development of efficient method for materials integration is important to ensure high-performance and reliable sensor operation. This work presents a direct and precisely controlled integration of graphene oxide (GO) using the electrospray deposition (ESD) onto a 10 MHz Quartz Crystal Microbalance (QCM) for humidity sensing. The proposed ESD method achieves a high mass resolution of a few nanograms. Moreover, the GO uniformly coats across the sensing electrode region as it acts as a ground electrode during ESD. The proposed ESD method also works for a wide range of nanomaterials, such as carbon nanotubes, tin oxide, and silicon carbide micro-and nano-powders. Compared to the conventional drop-casting and dip coating approaches, our method ensures minimal GO agglomeration, resulting in a stable QCM-oscillator operation in a wide range of relative humidity from 11% to 97%. The measurement sensitivity increases with an amount of GO, but less GO results in better noise and detection limit performances. The results shed light on the importance of selecting an optimal amount of sensing materials for stable sensor operations.     

月桂酰肌氨酸钠搭建阿尔法凝胶的方法研究及结构表征

阿尔法凝胶作为一种特殊的液晶结构，能够在清洁或调理皮肤的过程中给皮肤毛发提供更好的湿润感和调理性。由于阿尔法凝胶结构的搭建传统方法需要不少于14个碳原子的烷基表面活性剂，其实际应用一直受到限制。提供了一种由月桂酰肌氨酸钠作为烷基碳链为12个碳原子的氨基酸型表面活性剂搭建阿尔法凝胶的方法，并对其产物进行结构表征和分析。     

New insights into microstructural changes during transient liquid phase bonding of GTD-111 superalloy

The effects of joining temperature (T_J) and time (t_J) on microstructure of the transient liquid phase (TLP) bonding of GTD-111 superalloy were investigated. The bonding process was applied using BNi-3 filler at temperatures of 1080, 1120, and 1160 °C for isothermal solidification time of 195, 135, and 90 min, respectively. Homogenization heat treatment was also applied to all of the joints. The results show that intermetallic and eutectic compounds such as Ni-rich borides, Ni−B−Si ternary compound and eutectic-γ continuously are formed in the joint region during cooling. By increasing t_J, intermetallic phases are firstly reduced and eventually eliminated and isothermal solidification is completed as well. With the increase of the holding time at all of the three bonding temperatures, the thickness of the athermally solidified zone (ASZ) and the volume fraction of precipitates in the bonding area decrease and the width of the diffusion affected zone (DAZ) increases. Similar results are also obtained by increasing T_J from 1080 to 1160 °C at t_J=90 min. Furthermore, increasing the T_J from 1080 to 1160 °C leads to the faster elimination of intermetallic phases from the ASZ. However, these phases are again observed in the joint region at 1180 °C. It is observed that by increasing the bonding temperature, the bonding width and the rate of dissolution of the base metal increase. Based on these results, increasing the homogenization time from 180 to 300 min leads to the elimination of boride precipitates in the DAZ and a high uniformity of the concentration of alloying elements in the joint region and the base metal.     

Features of crystal structures and thermo-mechanical properties of weberites RE3NbO7 (RE=La,Nd, Sm,Eu, Gd) ceramics

The features of crystal structures, thermo-mechanical properties and their dominant mechanisms of weberites RE₃NbO₇ were studied as high-temperature oxides. We concentrated on connections between structures and thermo-mechanical properties, the influences of bond lengths, lattice distortion degrees and microstructures on these properties were estimated. The shortening of bond length and increment of bonding strength would lead to the increase of mechanical properties. The Vickers hardness (4.5-7.8 GPa) and toughness (0.5-1.6 MPa·m^1/2) of weberites RE₃NbO₇ are enhanced by grain refinement and increment of bond strength, while crystal structures, bond lengths, and lattice distortion degrees influenced their Young's modulus (100-170 GPa). Nano-indentation was applied to test the influence of microstructures on modulus and hardness. The dominant mechanisms for mechanical properties and thermal conductivity were proposed, which was conducive to properties tailoring and engineering applications of weberites RE₃NbO₇ oxides.     

利用菊池衍射花样鉴定晶体结构的方法研究

电子背散射衍射(Electron Backscatter Diffraction, EBSD)是研究材料显微结构的重要手段之一, 通过EBSD获取的菊池衍射花样是材料内部微观晶体结构的直观反映。本研究通过识别菊池花样中的对称轴, 结合晶体对称定律, 提出了一种利用菊池花样进行晶体对称性分析和晶体结构鉴定的方法。通过该方法成功对三个未知样品的对称性和晶体结构进行了判断。其中一个样品确定到所属晶系, 另两个样品锁定到部分点群, 通过确定晶系和点群排除了部分不符合对称性的相鉴定结果。研究结果表明, 利用菊池花样进行对称性分析是判断晶体结构的有效方法。同现有方法相比, 菊池衍射花样法大大缩小了相鉴定的检索范围, 显著提高了相鉴定的准确性和可靠性, 是一种有望用于新一代EBSD设备的标定技术。     

基于GIS单线图的配网停电单模拟操作应用研究

配电网停电会造成电力系统供配电可靠性以及服务质量下降,研究基于地理信息系统(GIS)单线图的配网停电单模拟操作应用。利用网格长度作为基本单位建立坐标系,以选取起始点与终止点为基础,通过四参数法将GIS坐标映射至图纸网格内,实现配网内设备初步布局,将杆塔、站房和整体均匀分布作为优化目标,设置多目标优化目标函数实现GIS单线图最终优化。选取某电力公司配网作为单模拟操作应用对象,模拟结果表明,单模拟操作配网停电后,该配网各负荷点年故障率、次平均停电时间以及年停电时间均有所减少,可有效提升配网的供配电可靠性。     

Optical properties of gadolinia-doped cubic yttria stabilized zirconia single crystals

Cubic zirconia single crystals stabilized with yttria and doped with Gd₂O₃ (0.10–5.00 mol%) were prepared by the optical floating zone method, and characterized by a combination of X-ray diffraction (XRD), and Raman, electron paramagnetic resonance (EPR), ultraviolet–visible (UV–Vis), photoluminescence excitation (PLE) and photoluminescence (PL) spectroscopic techniques. XRD and Raman spectroscopy showed that the crystal samples were all in the cubic phase, whereas the ceramic sample consisted of a mixture of monoclinic and cubic phases. The absorption spectrum showed four peaks at 245, 273, 308, and 314 nm in the ultraviolet region, and the optical band gap differed between samples with ≤3.00 mol% and those with >3.00 mol% Gd₂O₃. The emission spectrum showed a weak peak at 308 nm and a strong peak at 314 nm, which are attributed to the ⁶P_5/2 → ⁸S_7/2 and ⁶P_7/2 → ⁸S_7/2 transitions of Gd³⁺, respectively. The intensities of the peaks in the excitation and emission spectra increased with Gd³⁺ concentration, reached a maximum at 2.00 mol%, then decreased with higher concentrations. This quenching is considered to be the result of the electric dipole-dipole interactions, and this interpretation is supported by the Gd³⁺ EPR spectra, which showed progressive broadening with increasing Gd³⁺ concentration throughout the concentration range investigated.     

Alpha Synuclein only Forms Fibrils In Vitro when Larger than its Critical Size of 70 Monomers

The aggregation of α-synuclein into small soluble aggregates and then fibrils is important in the development and spreading of aggregates through the brain in Parkinson's disease. Fibrillar aggregates can grow by monomer addition and then break into fragments that could spread into neighboring cells. The rate constants for fibril elongation and fragmentation have been measured but it is not known how large an aggregate needs to be before fibril formation is thermodynamically favorable. This critical size is an important parameter controlling at what stage in an aggregation reaction fibrils can form and replicate. We determined this value to be approximately 70 monomers using super-resolution and atomic force microscopy imaging of individual α-synuclein aggregates formed in solution over long time periods. This represents the minimum size for a stable α-synuclein fibril and we hypothesis the formation of aggregates of this size in a cell represents a tipping point at which rapid replication occurs.